Experimental File Formats > BELPORE File Format

BELPORE datafiles are exported as text files with the extension .txt .

An example of the format readable by PoreXpert and PoreXY is shown below. The example is the PoreXY tutorial file MR3.txt , the context of which is given by the introduction to PoreXY.

PoreInspect REPORTING ;

Company name: ; X

Operator: ; X

;

TEST INFORMATION ;

Test date: ; 04-02-22

Sample name: ; MR3 polymer

Comment: ; Formkörper

Sample mass (g): ; 0.8023

Sample skeleton density (g/cm³): ; 0.0

Test file name: ; X

Combined with file (140): ; X

Mercury surface tension (N/m): ; 0.48

Mercury contact angle (°): ; 140.0

Test filling volume (mm³): ; 455.35

Starting hydr. press. of test (MPa): ; 0.013

(Dil+Hg+Sample) weight (g): ; 158.5344

Corrected weight (Dil.+Hg+Sample) (g): ; 158.3966

;

ANALYTICAL CONDITIONS ;

Maximum test pressure (MPa): ; 400

Increase speed: ; 6 - 19 MPa/min

Increase method: ; Pascal

Decrease speed: ; 7 - 28 MPa/min

Decrease method: ; Pascal

Temperature of test (°C): ; 28.5

Mercury density @ test (g/cm³): ; 13.5254

;

PREPARATION ;

Degassing time before filling (min): ; 8

Air pulses (N.): ; 1

Filling volume (mm³): ; 450.0

Preparation selection: ; AutoMatic

;

BLANK & DILATOMETER INFORMATION ; (Data from BELPORE HP file)

Blank date: ; 15-04-21

Blank filename: ; X

Comment ; blank

Blank Max pressure (MPa): ; 400

Blank Increase speed: ; 7 - 28 MPa/min

Blank Increase method: ; Pascal

Blank Decrease speed: ; 7 - 28 MPa/min

Blank Decrease method ; Pascal

Dil. number: ; 25

Dil. type: ; CD3

Dil. Cone length (mm): ; 28

Dil. Electrode gap (mm): ; 5

Dil. stem radius (mm): ; 1.5

Dil. weight (g): ; 61.0606

Temperature of blank (°C): ; 25.5

Mercury density @ blank (g/cm³): ; 13.5328

Blank filling volume (mm³): ; 445.16

Starting hydr. blank press. (MPa): ; 0.012796

(Dil+Hg) weight (g): ; 170.2889

RESULTS WITHOUT COMPRESSIB. CORR. ;

Total intruded volume (mm³/g): ; 358.351

at pressure of MPa: ; 399.8817

Bulk density (g/cm³): ; 0.8588 at pressure of MPa 0.013

Envelope density (g/cm³): ; 1.1542

at pressure of MPa: ; 2.0000

Intrud. Vol. (mm³): ; 239.029

Apparent density (g/cm³): ; 1.2407

at pressure of MPa: ; 399.8817

Spec. Vol. by skeleton dens. (mm³/g) Vd:; 0.000

Accessible porosity (%): ; 30.78

Inaccessible porosity (%): ; ---

EXPERIMENTAL DATA

Press. inc (MPa); Vol. inc (mm³/g); Press. dec (MPa); Vol. dec (mm³/g)

0.012993;0.000;399.882;358.351

0.013052;0.041;388.608;358.345

0.013227;0.083;385.026;358.345

0.013363;0.130;382.116;358.345

0.013507;0.183;379.751;358.345

0.013643;0.240;377.547;358.345

0.013749;0.298;375.682;358.345